Mechanical and Tribological Behavior of Unsaturated Polyester NanoCarbon Black Composite

Authors

  • Amer Hameed Majeed Material Engineering Department, Mustansiriyah University, Baghdad, Iraq Author
  • Mohammed S. Hamza Material Engineering Department, Mustansiriyah University, Baghdad, Iraq Author
  • Hayder Raheem Kareem Material Engineering Department, Mustansiriyah University, Baghdad, Iraq Author

Keywords:

compressive strength, flexural strength, hardness resistance, wear resistance, nanocarbon black, unsaturated polyester

Abstract

Experimental work had been done to demonstrate the effect of nanocarbon black particles (N220) contents on the mechanical and tribological behavior of unsaturated polyester nanocomposite prepared via the ultrasonic wave dispersion method. The results showed that the mechanical and tribological behavior was enhanced when the nanocarbon black particles content was increased up to 2%wt. and then decreased after that. The improvements in compressive strength and flexural strength are (16.13% at 2%wt. and 25.2% at 1%wt.), respectively, While The improvements in the hardness and wear resistance are (14.65% and 25.76% ) at 2%wt. , respectively.

Downloads

Key Dates

Published

2013-12-01

How to Cite

Hameed Majeed , A. ., S. Hamza, M. ., & Raheem Kareem, H. . (2013). Mechanical and Tribological Behavior of Unsaturated Polyester NanoCarbon Black Composite. Journal of Engineering and Sustainable Development, 17(6), 78-86. https://jeasd.uomustansiriyah.edu.iq/index.php/jeasd/article/view/1026